Rapid manufacturing system for metal, metal matrix composite materials and ceramics



РЕФЕРАТ

A product building system uses a stage movable in X-Y-Z directions for holding and moving a product. A fixed laser is focused on a spot on the products. Strips of materials are fed tangent to a forming direction from two sources on a rotating platform. The laser continuously or periodically welds and fuses a strip on the product. Relative motion bends the strip to the desired product shape. The laser cuts a strip and welds a new strip to form alternating layers. Side by side strips are butt-welded. Cores are formed differently from outer surfaces,using the continuous feeding, welding, fusing, bending, welding and fusing process. A mill on the rotating platform brings a mill end tool into contact with the layers to smooth lateral and upper surfaces.

Авторы:

Joshua E. Rabinovich (Newton, MA)

ID семейства патентов

25038197

Номер заявки:

 09/672,708

Дата регистрации:

29 сентября 2000 г.

Отсылочные патентные документы США

Application NumberFiling DatePatent NumberIssue Date
755214Nov 22, 19966144008

Класс патентной классификации США:

219/121.63

Класс совместной патентной классификации:

B22F 3/005 (20130101); B22F 3/008 (20130101); C04B 38/0006 (20130101); B23K 26/20 (20130101); B23P 15/04 (20130101); B23P 15/246 (20130101); B28B 1/00 (20130101); B28B 1/001 (20130101); B29C 67/0074 (20130101); C04B 38/0006 (20130101); C04B 35/00 (20130101); C04B 41/0036 (20130101); B29K 2995/0073 (20130101); B23K 2201/02 (20130101); B29C 2793/009 (20130101)

Класс международной патентной классификации (МПК):

B22F 3/00 (20060101); B23K 26/20 (20060101); B23K 26/00 (20060101); B23P 15/04 (20060101); B23P 15/24 (20060101); B29C 67/00 (20060101); B28B 1/00 (20060101); C04B 38/00 (20060101); B23K 026/20 (); B23K 026/34 ()

Область поиска:

;219/121.63,121.64,121.65,121.66,121.82

Использованные источники

[Referenced By]

Патентные документы США

4323756April 1982Brown et al.
5038014August 1991Pratt et al.
5121329June 1992Crump
5233150August 1993Schneebeli et al.
5312584May 1994Frasier et al.
5405660April 1995Psiuk et al.
5738817April 1998Danforth et al.
5900170May 1999Marcin, Jr. et al.
6156406December 2000Jang et al.
6269540August 2001Islam et al.
Главный эксперт: Heinrich; Samuel M.
Уполномоченный, доверенный или фирма: Wray; James Creighton Narasimhan; Meera P.

Текст решения-прецедента



This application is a division of application Ser. No. 08/755,214 filed Nov. 22, 1996 is now 6,144,008.

ФОРМУЛА ИЗОБРЕТЕНИЯ



I claim:

1. A product building apparatus comprising a frame, a laser beam source mounted on the frame, a beam expander and a mirror mounted on the frame, and a feedstock delivery module support mounted on the frame, a rotary stage mounted on the feedstock delivery module support and a rotary arm mounted on the rotary stage, plural feedstocks feeder mounted on the rotary arm and a laser beam focusing lens mounted on the rotary arm, plural feedstock storing spools mounted on the rotary arm and plural flat wire feedstocks stored on the spools, a feedstock nozzle connected to the rotary arm for receiving feedstock from one of the spools and feeders and for extending feedstock from a tip of the nozzle, the tip of the nozzle being aligned with a laser beam projected from the laser source to the mirror and through the support, rotating arm and rotary stage and lens, a stage positioned beneath the nozzle for receiving feedstock in a predetermined pattern according to relative movement of the stage and the feedstock delivery module in an X-Y direction for receiving the feedstock extending from the nozzle tip and for fusing the feedstock to a substrate or to a previously fused layer of the feedstock for constructing a model by depositing and fusing successive layers of the feedstock.

2. The apparatus of claim 1, wherein the spool, the rotary stage and the lens are aligned on an axis of the laser beam.

3. The apparatus of claim 1, wherein the feedstock feeders comprises pinch rollers driven by stepper motors.

4. The apparatus of claim 1, wherein the lens is mounted in a mount which is pivoted transverse to an axis of the laser beam, and further comprising a driver mounted on the rotary arm and connected to the lens mount for moving the lens mount along the pivot for traversing a laser beam spot across the feedstock for welding and cutting the feedstock.

5. The apparatus of claim 1, further comprising an inert gas passageway for flooding an intersection of the feedstock and the laser beam with inert gas during fusing of the feedstock.

6. The apparatus of claim 1, wherein the laser source produces a linearly polarized beam, and wherein the mirror converts the linearly polarized beam to a circularly polarized beam, and wherein the circularly polarized beam passes through the lens to the feedstock which has just been released from the nozzle.

7. The apparatus of claim 1, wherein the nozzle has a feedstock passageway with a radius in a feedstock passageway of the nozzle for bending the feedstock in a radius to release the feedstock tangent with the substrate or previous fused layer of feedstock.

8. The apparatus of claim 1, further comprising a computer having a multi axis controller for controlling the rectilinearly movable stage, the rotary stage and the feedstock feeder mechanism.

9. A product building apparatus, comprising a stage on which a product is built, a laser system for directing a laser beam on the product, an inert gas nozzle spaced from the stage for flooding with inert gas an impingement of the laser beam on the product, plural material storers spaced from the stage, a support spaced from the stage for supporting the gas nozzle, the material storers being positioned on the support, plural feeders mounted on the support and connected to the plural material storers for feeding the material to the product at an impingement of the laser beam on the product, a rotator connected to the support for rotating the material storers and feeds with respect to the product, and movers connected to the stage or to the support for relatively moving the stage or the support and laser system back and forth, side to side and up and down in X-Y-Z directions.

10. The apparatus of claim 9, further comprising a mill drive mounted on the support and a mill tool connected to the mill drive for positioning the mill tool against the product being constructed or the feedstock being delivered and milling a surface of the product or feedstock.

11. The apparatus of claim 9, wherein the material storers comprising first and second or multiple storage spools, and the first and second or multiple materials comprise first and second or multiple ribbons of material stored on the storage spools.

12. The apparatus of claim 9, wherein the laser system further comprises a laser head, a beam expander and a phase shift mirror for producing a laser beam, expanding the laser beam and redirecting the laser beam on the product.

13. The apparatus of claim 9, wherein the support comprises a fixed platform, a movable platform connected to the fixed platform for moving with respect to the fixed platform, and a drive connected between the fixed platform and the movable platform for moving the movable platform with respect to the fixed platform.

14. The apparatus of claim 9, further comprising a lens connected to the support for focusing the laser beam onto the product being built.

15. The apparatus of claim 9, wherein the material is a flat green ceramic fiber feedstock continuously fused, sintered and densified while the geometry of the part is being constructed, the shrinkage of the green feedstock being compensated by the controlled feed mechanism which allows the production of fully dense complex ceramic components with increased final part accuracy.

16. The apparatus of claim 9, wherein single multiple materials of metal and non metal are used.

17. The apparatus of claim 9, wherein the product is built from adjacent strips of distinct materials butt-welded in the same layer from the same or complementary feeders.

18. The apparatus of claim 10, wherein the product is built with laterally shifted layers and resulting stair steps are ground for smooth transition.

19. A product building apparatus comprising a frame, a laser beam source mounted on the frame, a beam expander and a mirror mounted on the frame, and a feedstock delivery module mounted on the frame, a rotary stage mounted on the feedstock delivery module support and a rotary arm mounted on the rotary stage, plural feedstocks feeder mounted on the rotary arm and a laser beam focusing lens mounted on the rotary arm, plural feedstock storing spools mounted on the rotary arm and plural flat wire feedstocks stored on the spools, a feedstock nozzle connected to the rotary arm for receiving feedstock from one of the spool and feeder and for extending feedstock from a tip of the nozzle, the tip of the nozzle being aligned with a laser beam projected from the laser source to the mirror through the support, rotating arm and rotary stage and lens, a stage positioned beneath the nozzle for receiving feedstock in a predetermined pattern according to relative movement of the stage and the feedstock delivery module in a X-Y direction for receiving the feedstock extending from the nozzle tip and for fusing the feedstock to a substrate or to a previously fused layer of the feedstock for constructing a model by depositing and fusing successive layers of the feedstock.


ОПИСАНИЕ




ПРЕДПОСЫЛКИ СОЗДАНИЯ ИЗОБРЕТЕНИЯ



The existing industrial era dominated by mass production is giving way to a new era or flexible manufacturing. Flexible manufacturing is a key manufacturing strategy for modern industries, in which complex shaped structural components are prevalent but quantity requirements are low, resulting in high unit costs and long lead times.

Rapid prototyping, or layered manufacturing is perhaps one of the most significant new technologies which enables the full realization of the power of modern Computer Aided Design (CAD) and Computer Aided Engineering (CAE) tools. CAD and CAE provide the concurrent design and analysis of a component in order to obtain the optimal structural layout and details about its material composition.

The materialization of such optimal designs requires unconventional manufacturing processes, such as layered manufacturing. This integrated product and manufacturing process development is especially critical in the modern industries such as aircraft, airspace, automotive and medical implants and prosthetics, to name a few.

The demand for an affordable, high strength, lightweight complex components, capable of operating at elevated temperatures and in adverse environments, requires continuous efforts in advanced structural designs, new materials and manufacturing processes.

To meet these requirements, materials such as Titanium and continuous fiber Titanium Matrix Composites, which have stable high specific strength properties at elevated temperatures, must be implemented, and the fabrication technology to incorporate these materials into lightweight structural concepts must be developed.

The stumbling block toward the wide use of these materials has been the very high cost of the existing manufacturing methods used for the production of components from such materials. For example, titanium is difficult to machine and requires fabrication processes such as the Superplastic Forming and Codiffusion Bonding (SPF/DB) of titanium sandwich structuring. These fabrication processes require high tooling costs and long lead time.

Even more complex and expensive multi-step methods are used for the production of MMC components, such as foil/fiber layering with High Isostatic Pressure (HIP) consolidation. Very high capital and running costs are typical for these manufacturing processes.

Rapid Prototyping or Free Form Fabrication is present one of the fastest developing manufacturing technologies in the world. Free Form Fabrication through layered material deposition has proved to be an attractive method for 3D object generation. The layered part buildup offers the possibility of expanding the implementation of advanced designs with respect to part complexity, multi-layer multi-material structures, and the optimal material distribution within the desired part.

Although significant improvements in application of high temperature structural materials have been achieved with such processes as SLS, Thermal Spray Shape Deposition and 3D welding, a number of inherent processing limitations prevents them from producing parts with structural integrity and accuracy readily obtainable by conventional manufacturing methods.

One of the main shortcomings of Thermal Spray Shape Deposition and 3D welding methods is the requirement for the liquefaction of the feedstock material prior to its spay or cladding deposition, which results in high energy deposition, large residual stresses, poor mechanical properties, layer debonding, and part distortions. In the case of metal powder sintering, the main shortcomings are the limited choice of specially prepared multiphase metal powder materials with limited physical and mechanical characteristics. The fabricated parts have low density and require a time consuming and expensive postprocessing. The part accuracy is unpredictable due to significant shrinkage after postprocessing.

In the Sheet Lamination Process as applied to metal layers deposition, the process is limited to layers joining by bonding or soldering. Attempts to use welding as a layer joining method proved to be difficult.

None of those processes lends itself to the production of continuous fiber MMC materials.

Extensive research efforts for the development of Rapid Prototyping technologies capable of producing metal and composite materials are being conducted within academic institutions and industry throughout the world. The USA leads the research community in this field, but in the last several years the research conducted in Europe has intensified, particularly in the area of rapid prototyping in metals. Several rapid prototyping processes, such as Thermal Spray Shape Deposition, 3D welding, Sheet Lamination Process and especially SLS, have progressed in the application of metal materials.

Originally, the process of Selective laser Sintering (SLS) was developed by the University of Texas at Austin. DTM Corporation has developed this process into a multi-step called RapidTool process that is capable of producing metal parts. It is a time consuming process for molding making using plastic coated iron based metal powder. Current research is being conducted on two-phase metal powder material such as Bronze-Ni.

SLS's main shortcomings are the limited choice of specially prepared multiphase metal powder materials with limited physical and mechanical characteristics. The fabricated parts have porosity and require a time consuming and expensive postprocessing. Part accuracy is unpredictable due to significant shrinkage after postprocessing.

Other related work is Thermal Spray Shape Deposition, 3D Welding and Laser Cladding.

Carnage Mellon University uses an arc-spray system in which two melted wires are sprayed onto a substrate to generate a part layer.

The University of Nottingham in the U.K. uses a MIG welding torch which melts a 0.8 mm feed wire with a current of 100 A and deposits it in the shape of a bead of weld that is approximately 4.5 mm wide and 1.4 mm thick. Using this technology, these dimensions represent the resolution of the system.

IPT in Germany is working on a metal part generation process with laser cladding which involves directing a high power laser (700 W CO) onto the substrate, and simultaneously melting the powder or wire feedstock at the laser spot.

One of the main shortcomings of Thermal Spray Shape Deposition, 3D welding and Laser Cladding methods is the requirement for the liquefaction of the feedstock material prior to its spray or cladding deposition, which results in high heat buildup, large residual stresses, poor mechanical properties, layer debonding, and part distortions.

SLS as well as 3D Printing processes have the promise of mixing fiber reinforcing particulates into a powder mix (SLS) or into ceramic slurry (3D printing), thus enabling the production of MMC or CMC components.

None of those processes lends itself, though, to the production of continuous fiber reinforced MMC materials which dominate military applications because of their superior performance/cost characteristics.


СУЩНОСТЬ ИЗОБРЕТЕНИЯ



The Solid Feedstock Free-Form Deposition (SFFD) System addresses those limitations by using a proprietary process developed for a free form deposition of a full density metal feedstock without its prior liquefaction. The result is significantly lower energy deposition for the fusion process, thus the reduction of internal stresses, and the improvement in the part accuracy. There is no requirement for a part postprocessing and the part accuracy is comparable with the accuracy achieved by such conventional manufacturing processes as milling and turning.


КРАТКОЕ ОПИСАНИЕ РИСУНКОВ



FIG. 1 shows a rapid manufacturing system of the present invention.

FIG. 2 is a detail of the nitrogen nozzle and feedstock delivery nozzle.

FIG. 3 is a schematic representation of a controller.

FIG. 4 is a cross-sectional detail of an alternate layer buildup of a continuous filament fiber reinforced metal matrix composite.

FIG. 5 shows the construction of a compressor blade.

FIGS. 6 and 7 are details of a buildup of components of FIG. 8 without and with milling.

FIGS. 8 and 9 are respectively a vertical cross-section and a horizontal cross-section taken along line C--C of FIG. 8 showing a built up parabolic nozzle having separated walls and joining sections.

FIG. 10 is a cross-sectional plan view of a three-dimensional article made with a honeycomb interior taken along line B--B of FIG. 11, all formed by the present invention.

FIG. 11 is a cross-sectional elevation taken along line E--E of the structure shown in FIG. 10.

FIGS. 12A and 12B are elevational and end views of a structure made according to the present invention.

FIGS. 13 and 14 are cross-sectional details of multiple and alternating layer products of the present invention.

DETAILED DESCRIPTION OF THE DRAWINGS

Referring to FIG. 1, a laser head 1 is supported on a frame for projecting a laser beam 2 through a beam expander 25 onto a phase shift mirror 3, which is also supported on a frame. The redirected beam 4 is directed through a rotary assembly and into a focusing lens 5, which focuses the beam energy on the product 12 as it is being formed on stage 10. The feedstock 7 is delivered from a reel 6 through feed rollers mounted on the end of feed motor 9. The reel and feed structures are mounted in a frame 8, which is mounted on a rotary stage 11. The rotary stage 11 is driven in a direction shown by the arrows C by a motor and reduction gear shown at rear of stage 11. A milling motor drives the mill 31, shown enlarged at the left, which is used to maintain the flatness of the top layer of the product 12. The mill motor and shaft assembly may be rotated through an angle a as shown to produce a chamfer on the edge of the feedstock. This provides a smooth transition between the shifted current layer and the previous layer, as shown in FIG. 9. The stage 10 is moved in X, Y and Z directions, as shown at 13. Feedstock preparation station 35 is maintained for preparation of the wire prior to deposition. Actuators keep station 35 in the focused plane of the laser. The mill 31 may be brought to the product. Preferably the table is moved in the X and Y direction to bring the product into contact with the mill. Additional or alternative feedstock material is held on a reel 32, which is similar to reel 6. A similar feedstock drive 9 may be mounted on a similar frame 8 beneath the reel 32. Moving stage 22 is used to relatively position the laser beam, focusing lens and gas nozzle assembly with respect to the feedstock delivery system. Inert gas such as nitrogen or argon is introduced through inlet 16.

In large constructions the product holding stage may remain stationary, and the laser beam and feedstock delivery system move in X, Y, Z directions while the feedstock delivery system rotates.

As shown in FIG. 2, the gas is delivered through a nozzle 20 which surrounds the beam to flood the welding area of the feedstock which is delivered from the feedstock delivery nozzle 21.

FIG. 3 shows a controller 14 with a multiple access controller with outputs to the laser head 1 and to the feedstock drive 9, the rotary stage drive 11 and the feed positioning actuators 22, as well as to the X, Y, Z stage 13, as shown in FIG. 1. The controller 14 shown in FIG. 3 also has a multi-functional card 13, which supplies outputs to the mill 30 and to the inner gas control input 16.

Depending on the aspect ratio of a feedstock profile, the new process permits building overhang structures up to about 15 degrees of the horizontal without any support structures. For example, with a feedstock size of 0.010" thick and 0.040" wide an overhang wall can be built about 18.degree. to the horizontal without support structures.

The SFFD process lends itself to the production of continuous filament fiber-reinforced metal matrix composite (MMC) materials by alternating various materials within the part's cross-section.

The example in FIG. 4 shows how the process can be utilized for fabrication of MMC components using a metal flat wire feedstock having 0.020" width and 0.010" thickness, and a pre-impregnated carbon fiber tape having 0.040" width and about 0.010" thickness. The component has a shell, with the wall of the shell being about 0.085" thick. The wall is constructed so that the outer surfaces (strands 41 and 43) are built out of metal and the internal wall structure is a combination of a continuous carbon fiber tape 42 layered between the metal strips.

The operation of the SFFD System is explained based on the example of the fabrication of a complex cross-section profile, such as the aircraft compressor blade airfoil depicted in FIGS. 4 and 5. On the basis of the blade cross-sections represented in CAD software, a feedstock path 39 is generated by following the boundaries and the pattern defining the part's layers. The interior 44 of the blade is hollow. The wall 45 is built as shown in FIG. 4.

Prior to fusion of feedstock strand onto a substrate, the end shape of the feedstock is precut if necessary.

FIG. 4 shows a cross-section of the wall of the part's shell built on the SFFD System. The arrows on FIG. 5 show the feedstock nozzle orientation and the feedstock delivery direction 39 during the layer buildup. The system's rotational range is +/-360.degree. or multiples thereof. Parts may be built spirally.

Stairsteps is one of the accuracy problems common to a layered or laminated part buildup. The operation of an end mill (31, FIG. 1) device removes 51 stairsteps 52 from overhang structures such as shown in FIGS. 6 and 7. The milling feature may be used for the removal of the "stairstepping effect" existing in any layered manufacturing. FIG. 8 shows a part which would have "stairstepping effect" shown in FIG. 6. The stairstepping is removed as shown in FIG. 7 with a milling tool 31 shown in FIG. 1. The milling tool has an angular adjustment for changing the chamfer angle to accommodate for various degrees of "stairstepping". The same tool, for example an end mill, can be used for cleaning the top surface of the newly deposited layer in order to maintain the latest layer flatness and tolerance in the Z direction. The latter function of that end mill tool can be performed by a separate grinding wheel tool, which is a faster way to clean the top surface of the layer. That feature may be used during the production of a complex 3-D part--a coaxial parabolic nozzle, out of titanium, shown in FIGS. 8 and 9. The part has base outside and inside diameters of 1.25" and 1" and is 1" high.

FIGS. 8 and 9 show a nozzle having inner and outer layers 61 and 63 separated by bridging 65, which is butt welded 67 to the inner and outer layers as the layers and bridging are formed.

FIGS. 10 and 11 show structures formed of multi-strand exterior walls 71 and butt welded honeycomb interiors 73.

FIGS. 12A and 12B are elevational and end views of a beam structure 75 made according to the present invention. The beam may have a composite structure such as, for example, shown in FIGS. 4, 13 and 14, or may have a honeycomb interior such as shown in FIGS. 10 and 11. The beam may be made of layers of laser-fused and hardened ceramic materials. Because of immediate rigidification, all material reformation is compensated as the strands are guided on the product.

The invention is directed to fusing or sintering feedstock materials in any combination. Separate metal or nonmetal feedstock materials are used for fabricating strictly metal or strictly nonmetal parts. Simultaneous use of metal and nonmetal may be used in multiple feedstocks. By alternating the materials within a cross-section, composite material parts are fabricated. Composite material parts can also be fabricated by using a single feedstock material which comprises the combination of metal and nonmetal.

The invention produces solid models out of a wide range of metal, nonmetal and composite materials. Materials such as Titanium, Ni--Cr stainless steel alloys, glass, polypropylene and polyethylene are readily available in the form of wire, fibers or strips, and have been laser welded and cut with excellent results. When the continuity of the feedstock must be interrupted, the deposited laser energy is increased to the level sufficient for the feedstock cut.

Although there is a wide range of metal and non-metal materials of potential interest that can be used in the SFFD process, a limited number of materials and their combinations is described. Materials such as Titanium, 304 SST and Graphite Fiber Epoxy Prepreg Tape are the materials that are described herein.

In addition, cermets and ceramic materials may be used.

Metal and nonmetal materials, as well as a new class of materials such as cermet materials, may be used.

The competing rapid manufacturing technologies produce layered ceramic parts by first extruding "green" ceramic slurry (ceramic particles plus liquid binder) to generate the desired part, then the "green part" is sintered by placing the part into high temperature and high pressure environment. After that furnace treatment to bake out the binder material and to densify the part. Warpage and distortion due to material shrinkage limit the attainable accuracy of the final parts. There are commercially available "green" ceramic fibers generally available in a round cross-section shape and which are sufficiently ductile to extrude them within the feed mechanism into a shape with two opposite flat sides.

The present process allows deposition of the "green" flat fibers similar to the deposition of the metal flat wire.

A significant advantage of the present process of the deposition of a "green" ceramic material and the part building is in the simultaneous deposition, evaporation of the binder material and sintering. The material's sintering and densification occur during the feedstock fusion process. The simultaneous feedstock fusion, sintering and densification are occurring while the geometry of the part is being constructed.

Because the mass of the material being sintered is confined to a small section of a thin fiber affected by the energy source beam spot, the cooling of this small region of the fiber is fast. The effect of material shrinkage resulting from the sintering is incorporated into the process of the part construction, with a minimal effect on the accuracy of the final part. The final part accuracy will not be effected by post construction heat treatment, as is the case with the competing technologies.

Titanium is an attractive metal for aircraft structural components for several reasons: high temperature capability (1000.degree. F.), low density, high strength and stiffness, high damage tolerance, and corrosion resistance. Titanium has excellent laser weldability, and therefore it has good potential for the application of the SFFD processes.

MMC materials offer a number of advantages over conventional metals. Their superior lightness, strength and stiffness aid in improving aircraft payload-range capability, and can provide the opportunity to downsize subsystems. Unidirectional graphite fiber epoxy prepreg tape with cross-section of 0.010".times.0.040" may be used.

The MMC products may be fabricated following the layers lay up configuration shown in FIGS. 13 and 14. For example, 0.degree. metal, 90.degree. metal, 0.degree. metal and graphite, 0.degree. metal, 90.degree. metal and graphite, several repeats of the last two alternatives, and finally 0.degree. metal, as shown in FIG. 13. Special attention during this process insures a proper inert environment in the vicinity of graphite fiber during fusion in order to prevent its oxidation and damage.

As applied to the performance of the new SFFD System, and considering a feedstock thickness of 0.010" to 0.020" thick and 0.020" to 0.040" wide, welding speeds of 100 to 300 in./min. can be achieved. That may be realized in a rate of metal deposition between 1.6 lb/hr. to 2.3 lb/hr. Clearly, the rate of deposition also depends on the part geometry and can be improved by proper selection of the feedstock thickness and width as applied to a particular component.

The high rate of metal deposition in the new SFFD process is combined with the laser's ability to perform low-heat-input welding operations. The key to understanding this laser capability is in considering the laser's operating pulse width. For example, consider a laser operating at the parameters of 10 Joules, 4 ms pulse and 10 Hz, the average power is 100 W (10 J.times.10 Hz) and the pulse peak power is 2.5 kW (10 J/4 ms). Thus, a very small amount of energy is enough to perform the weld process.

The new SFFD process fully utilizes this basic advantage of low-heat-input laser welding with the resulting low heat buildup and low distortions, and combines it with the proprietary precision controlled feedstock shape contouring capabilities. That results in a superior method of affordable manufacturing of complex structural titanium and MMC components with high production rates, and a truly rapid manufacturing process.

A fully automated Rapid Manufacturing--Free Form Fabrication System capable of producing affordable, complex 3-D structural components from metals and continuous filament metal-matrix composite (MMC) materials is based on a full density metal deposition process and system to produce continuous filament metal--matrix composite materials. Evaluation of sample 3-D parts produced on the system directly out of nickel alloy indicates the process' capabilities and its application in rapid and affordable manufacturing of complex metal and MMC components.

One element of the new system is the Solid Feedstock Free-form Deposition (SFFD) process in which a solid flat feedstock of metal or nonmetal material is laser fused onto a substrate, while simultaneously being formed into a desired geometrical shape.

Because the feedstock is a full density material and its fusion to a substrate is performed in conventional modes of laser welding, no liquefaction is required prior to the material deposition. That results in a significant reduction in energy deposited during the fusion process, which means reduced internal residual stresses in the part, less deformation, and better accuracy of the part.

The present invention provides the capability of fusion of the feedstock side to the side of the adjacent feedstock in the same layer. The scanning of the energy beam transverse to the feedstock long axis allows the butt welding of the adjacent sides. That provides for multiple passages of the feedstock in the same layer.

The beam scanning occurs not only across the feedstock, but also along the feedstock's long axis. The additional movement allows butt welding of the feedstock end to the previously laid feedstock pass in the same layer, as shown in FIGS. 9 and 10.

The following capabilities of the new process show its affordability, high production rate, and set it apart from the existing Rapid Manufacturing processes: a. No postprocessing is required. The proper choice of laser welding parameters assures high quality, low Heat Affected Zone welding having the mechanical characteristics equal to the base material. The result if less residual stress and higher accuracy parts, savings on expensive postprocessing tooling, and in production cycle time. b. The use of a flat solid feedstock allows the production of parts with large "overhang" structures without the need for time consuming "sacrificial material layers" or support structures used in other Rapid Manufacturing methods. c. The materials of construction are of full density as opposed to powder sintered materials where porosity is always present. d. There is the capability of producing continuous fiber MMC materials at room temperature and pressure and with precision control of spacing of fibers.

FIG. 1 depicts the new SFFD System. FIGS. 4-14 show examples of complex 3-Dimensional 304 SST parts that can be produced on the system. A fully functional SFFD System incorporates the above-mentioned features and capabilities. The new Multiple Feedstock Module (MFM) affects the system's resolution and overall accuracy of fabrication, the higher power laser and its effect on the quality and speed of fusion.

Multiple-Material deposition techniques as well as Graphite Fiber Tape deposition and encapsulation techniques are used. Graphite tape/metal cavity placement provides the possibility of a reliable placement of the graphite tape into the metal cavity and its subsequent fusion bonding onto the substrate.

The system is used to manufacture metal and MMC complex shapes such as honeycomb structures and other features found in complex structural components.

While the invention has been described with reference to specific embodiments, modifications and variations of the invention may be constructed without departing from the scope of the invention, which is defined in the following claims.

* * * * *